Product Description

Aquaprufe TPO Waterproof Membrane

Thermoplastic polyolefin (TPO) membrane is a type of polymer waterproof material based on polypropylene(PP) and rubber, prepared by existing technique. It is recycling throughout its service life (from its production till the end of its service life). There isno chlorine, heavy metal nor elements harmful to the roots and it is environmental friendly.

PRODUCT FEATURES

  • Excellent weather resistance, aging resistance, tensile strength and elongation.
  • Operation can be done on wet substrate. Directly expose to the weather conditions without any protective layer. Simple construction. No contamination.
  • Repeat welding is possible.
  • White color TPO to increase reflection of sun rays.
  • Ability of resist the growth of mould and alga.

WHERE TO USE

Mainly apply to the roof water proofing construction of industrial, civil and public buildings.

Membrane reinforced with mesh ( TPO-P) is applied to the single ply roof water proof system by mechanical fastening.

Membrane with underlying layer of fabric ( TPO-L) is applied to the concrete substrate byfull adhesion waterproof system.

Homogeneous membrane (TPO-H) is applied to the flashing area.

SPECIFICATION

Nominal length: 15m, 20m, 25m

Nominal width: 1000mm, 2000mm

Thickness: 1.2mm, 1.5mm, 1.8mm 2.0mm

Other specifications are possible bythe confirmation of supply and requisitioning parties. The thickness is notless than 1.2mm.

DATE BASEIMPLEMENTED STANDARD: GB/T23457-2009

No.

Item

index

H

L

P

1

Thickness Above Scrim

——

0.40

2

tensile performance

Max.Tensile strength, (N/cm)≥

——

200

250

Tensile Strength, MPa≥

12

——

——

Elongation at max. tensile strength. %≥

——

——

15

Elongation at break, %≥

500

250

——

3

Dimensional change after heat treatment

2.0

1.0

0.5

4

Flexibility at low temperature

-40, no cracking

5

Water tightness

0.3MPa, 2h, water tight

6

Puncture Resistance

0.5kg·m, impermeable

7

Hydrostatic Resistance

——

20kg, impermeable

8

Lap seam peeling strength

4.0 or membrane breakage

3.0

9

Right-angled tear strength

60

——

——

10

Trapezoid tear strength

——

300

450

11

Water absorption(70, 168h), %

After immersion≤

4.0

After drying≤

-4.0

12

Heat aging

Period,h

672

Appearance

no bubbling ,crack, layered, bonding nor hole

Retention rate at max. tension, %≥

90

Elongation retention rate at max tension, %≥

90

Flexibility at Low temperature

-40, no cracking

13

Chemical resistance

Appearance

no bubbling ,crack, layered, bonding nor hole

Retention rate at max. tension, %≥

90

Elongation retention rate at max tension, %≥

90

Flexibility at Low temperature

-40, no cracking

14

Artificial weathering aging

Period,h

1500

Appearance

no bubbling ,crack, layered, bonding nor hole

Retention rate at max. tension, %≥

90

Elongation retention rate at max tension, %≥

90

Flexibility at Low temperature

-40, no cracking

a. The Hydrostatic Resistance is only applicable for the pressed roofing.
b. The period for the artificial weather aging test is 2500 h for the single ply roofing system.